- Schmolz + Bickenbach UgiPermâ„¢ 12FM Stainless Steel Bar
Schmolz + Bickenbach UgiPermâ„¢ 12FM Stainless Steel Bar
| Category | Metal , Ferrous Metal , Ferritic , Stainless Steel |
| Manufacturer | Schmolz + Bickenbach (Swiss Steel International) |
| Trade Name | UgiPerm™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schmolz + Bickenbach UgiPermâ„¢ 12FM Stainless Steel Bar.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UgiPerm™ 12FM is a 12% chrome ferritic stainless with improved magnetic properties designed for use in electro-injectors, valves and many other applications. The grade was developed for magnetic applications requiring a very low coercive magnetic field (Hc) and a very high permeability. UgiPerm™ 12FM has a high level of electrical resistivity that shortens activation time when used in pulse mode. It offers excellent magnetic properties with superior corrosion resistance no offered by iron alloys.Applications: Solenoid valves, fuel injectors, irrigation valves, magnetic sensors, magnetic brakes, and electro-mechanical devices.Magnetic Properties (Heat Treatment): Uniformly heat at 800°/900°C (1470°F/1650°F) for 2 hours, then cool to 500°C (930°F) at a rate of 50°C (120°F) per hour. The cycle should be done in a dry hydrogen or vacuum atmosphere to prevent oxidation.Information provided by Schmolz + Bickenbach
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.72 g/cc | 0.279 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 87 - 92 | 87 - 92 | |
| Tensile Strength | 448 - 552 MPa @Thickness <=25.4 mm |
65000 - 80000 psi @Thickness <=1.00 in |
Cold Drawn Bar |
| Tensile Strength, Yield | 310 - 448 MPa @Strain 0.200 %, Thickness <=25.4 mm |
45000 - 65000 psi @Strain 0.200 %, Thickness <=1.00 in |
Cold Drawn Bar |
| Elongation at Yield | >= 30 % @Thickness <=25.4 mm |
>= 30 % @Thickness <=1.00 in |
Cold Drawn Bar |
| Reduction of Area | >= 60 % @Thickness <=25.4 mm |
>= 60 % @Thickness <=1.00 in |
Cold Drawn Bar |
| Modulus of Elasticity | 200 GPa | 29000 ksi | Tension |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.3 µm/m-°C @Temperature 20.0 - 100 °C |
5.75 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 10.8 µm/m-°C @Temperature 20.0 - 204 °C |
6.00 µin/in-°F @Temperature 68.0 - 400 °F |
||
| 11.5 µm/m-°C @Temperature 20.0 - 299 °C |
6.40 µin/in-°F @Temperature 68.0 - 570 °F |
||
| 11.7 µm/m-°C @Temperature 20.0 - 432 °C |
6.50 µin/in-°F @Temperature 68.0 - 810 °F |
||
| 12.2 µm/m-°C @Temperature 20.0 - 499 °C |
6.80 µin/in-°F @Temperature 68.0 - 930 °F |
||
| Thermal Conductivity | 21.9 W/m-K @Temperature 20.0 °C |
152 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.020 % | <= 0.020 % | |
| Chromium, Cr | 11.5 - 12.5 % | 11.5 - 12.5 % | |
| Iron, Fe | >= 83.44 % | >= 83.44 % | |
| Manganese, Mn | 0.30 - 0.50 % | 0.30 - 0.50 % | |
| Molybdenum, Mo | 0.25 - 0.75 % | 0.25 - 0.75 % | |
| Nickel, Ni | >= 0.50 % | >= 0.50 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Silicon, Si | 1.0 - 2.0 % | 1.0 - 2.0 % | |
| Sulfur, S | 0.15 - 0.25 % | 0.15 - 0.25 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000780 ohm-cm | 0.0000780 ohm-cm | |
| Magnetic Permeability | 2000 - 3000 | 2000 - 3000 | |
| Magnetic Coercive Force, Hc | 1.2 - 1.6 Oe | 1.2 - 1.6 Oe | |
| Magnetic Saturation Flux Density, Bmax | 17000 Gauss | 17000 Gauss | |
| Magnetic Remanence, Br | 5000 - 7000 Gauss | 5000 - 7000 Gauss | |
| Curie Temperature | 732 °C | 1350 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Annealing Temperature | 699 - 799 °C @Time 3600 sec |
1290 - 1470 °F @Time 1.00 hour |
Soft; Air cool |
| Hot-Working Temperature | 482 °C | 900 °F | Flow Stress of 110 MP at 3.6s<sup>-1<sup> |
| 538 °C | 1000 °F | Flow Stress of 65 MP at 3.6s<sup>-1<sup> | |
| 593 °C | 1100 °F | Flow Stress of 40 MP at 3.6s<sup>-1<sup> | |
| 649 °C | 1200 °F | Flow Stress of 25 MP at 3.6s<sup>-1<sup> | |
| 749 - 1200 °C | 1380 - 2190 °F | Uniformly heating |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Corrosion Resistance | Humidity | 3/4 |
| NaCl 0.2g/l | 1.65% mass loss; 60°C; 500 hrs | |
| NaCl 0.4g/l | 1.6% mass loss; 60°C; 500 hrs | |
| NaCl 0.6g/l | 2.4% mass loss; 60°C; 500 hrs | |
| Nitric Acid | 2/4 | |
| Sodium Carbonate | 2/4 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® PC1000R PC (Asia Pacific)
- Materion Beryllium Copper Alloy 25 Strip; A -Planished (TB00) Temper (UNS C17200)
- Freudenberg Simrit V75 Standard Fluoroelastomer
- SYNTHOS Krasten® 152 General Purpose Polystyrene
- Styrolution Luran® S 776 SE ASA
- SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Europe-Africa-Middle East)
- Tra-Con Tra-Bond FDA22BK01 Food and Drug Application Epoxy Adhesive
- 3M PS193 White Yupo™ TIS Label Products
- Addiplast Addinyl A2 ZG30 Nylon 66, 30% Glass Bead
- Latrobe LSS™ A6 Tool Steel (ASTM A6)
Copyright © lookpolymers.com All Rights Reserved