Schmolz + Bickenbach Thermodur® 2714 Extra Fine Structure - Hot Work Die Steel

Category Metal , Ferrous Metal , Tool Steel , Hot Work Steel
Manufacturer Schmolz + Bickenbach (Swiss Steel International)
Trade Name Thermodur®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schmolz + Bickenbach Thermodur® 2714 Extra Fine Structure - Hot Work Die Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Thermodur 2714 is an Extra Fine Structure (EFS) nickel based tool steel.Characteristics: Excellent high temperature strength; Good toughness; and Good resistance to thermal shockApplications: Forging dies, Die holders, Die rings, Hydroform tooling, Plastic tooling, and Wedge blockStress Relieving (Heat Treatment): 1000°F for 2 hours; Cooling: Cool slowly to 800°F in air; Hardness:
Physical Properties Metric English Comments
Density 7.78 g/cc
0.281 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell C 32

@Treatment Temp. 650.0 °C,
Time 7200 sec
32

@Treatment Temp. 1202 °F,
Time 2.00 hour
36

@Treatment Temp. 600.0 °C,
Time 7200 sec
36

@Treatment Temp. 1112 °F,
Time 2.00 hour
40

@Treatment Temp. 550.0 °C,
Time 7200 sec
40

@Treatment Temp. 1022 °F,
Time 2.00 hour
43

@Treatment Temp. 500 °C,
Time 7200 sec
43

@Treatment Temp. 932 °F,
Time 2.00 hour
45

@Treatment Temp. 450 °C,
Time 7200 sec
45

@Treatment Temp. 842 °F,
Time 2.00 hour
47

@Treatment Temp. 400 °C,
Time 7200 sec
47

@Treatment Temp. 752 °F,
Time 2.00 hour
Tensile Strength 1210 MPa
175000 psi
40-42 HRC
1340 MPa
195000 psi
42-44 HRC
1590 MPa
230000 psi
44-48 HRC
503 MPa

@Temperature 600.0 °C
73000 psi

@Temperature 1112 °F
1170 MPa

@Temperature 400 °C
170000 psi

@Temperature 752 °F
1410 MPa

@Temperature 200 °C
205000 psi

@Temperature 392 °F
Tensile Strength, Yield 296 MPa

@Temperature 1112 °C
43000 psi

@Temperature 2034 °F
965 MPa

@Temperature 752 °C
140000 psi

@Temperature 1390 °F
1210 MPa

@Temperature 392 °C
175000 psi

@Temperature 738 °F
1030 MPa

@Strain 0.200 %
150000 psi

@Strain 0.200 %
40-42 HRC
1190 MPa

@Strain 0.200 %
172000 psi

@Strain 0.200 %
42-44 HRC
1370 MPa

@Strain 0.200 %
198000 psi

@Strain 0.200 %
44-48 HRC
Elongation at Yield 13 %
13 %
44-48 HRC
15 %
15 %
42-44 HRC
16 %
16 %
40-42 HRC
Reduction of Area 38 %
38 %
44-48 HRC
40 %
40 %
42-44 HRC
45 %
45 %
40-42 HRC
45 %

@Temperature 392 °C
45 %

@Temperature 738 °F
50 %

@Temperature 752 °C
50 %

@Temperature 1390 °F
85 %

@Temperature 1112 °C
85 %

@Temperature 2034 °F
Thermal Properties Metric English Comments
CTE, linear 12.6 µm/m-°C

@Temperature 21.1 - 93.3 °C
7.00 µin/in-°F

@Temperature 70.0 - 200 °F
13.5 µm/m-°C

@Temperature 21.1 - 204 °C
7.50 µin/in-°F

@Temperature 70.0 - 400 °F
13.5 µm/m-°C

@Temperature 21.1 - 399 °C
7.50 µin/in-°F

@Temperature 70.0 - 750 °F
Thermal Conductivity 36.6 W/m-K

@Temperature 21.1 °C
254 BTU-in/hr-ft²-°F

@Temperature 70.0 °F
37.2 W/m-K

@Temperature 204 °C
258 BTU-in/hr-ft²-°F

@Temperature 400 °F
37.5 W/m-K

@Temperature 399 °C
260 BTU-in/hr-ft²-°F

@Temperature 750 °F
Component Elements Properties Metric English Comments
Carbon, C 0.56 %
0.56 %
Chromium, Cr 1.1 %
1.1 %
Iron, Fe 96.04 %
96.04 %
Molybdenum, Mo 0.50 %
0.50 %
Nickel, Ni 1.7 %
1.7 %
Vanadium, V 0.10 %
0.10 %
Processing Properties Metric English Comments
Annealing Temperature 760 - 773.9 °C
1400 - 1425 °F
Soft; Cooling: 1 hr/in/max 6hrs; Cool to 1260°F and hold 4 hrs and let furnace cool to 800°F; < 250 HB
Copyright © lookpolymers.com All Rights Reserved