Samsung Cheil Industries Starex® TF-0959 T HI-PMMA
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® TF-0959 T HI-PMMA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 220 °C |
16 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 54.9 MPa | 7970 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 79.4 MPa | 11500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.31 GPa | 336 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.45 J/cm @Thickness 6.35 mm |
4.59 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C @Thickness 6.40 mm |
171 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 92.0 °C | 198 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.50 % @Thickness 2.50 mm |
0.50 % @Thickness 0.0984 in |
ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pencil Hardness | 3H | 500g, JIS K 5401 |
Users viewing this material also viewed the following:
- Abatron 810328 A/B Filled Potting Compound (discontinued **)
- ExxonMobil OPTEMA™ TC 140 Molding, extrusion, compounding and adhesive resin (discontinued **)
- Fujipoly Industries Sarcon® GR-L Gap Filler Pad
- Henkel Turco Mil Etch Etchant
- Shakespeare NX-806 Saltwater Nylon Copolymer Fishing Line, 130 lb
- SABIC Innovative Plastics LNP VERTON RX10409D PA 66
- Arlon R37053W007 0.007" (0.178 mm) Cured Silicone Rubber with Fiberglass Substrate
- PolyOne Synprene® ST-6250 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved