SSAB Tunnplat Domex® 355MC HSLA Steel
| Category | Metal , Ferrous Metal , Alloy Steel , Low Alloy Steel |
| Manufacturer | SSAB Tunnplat AB |
| Trade Name | Domex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SSAB Tunnplat Domex® 355MC HSLA Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
HSLA SteelCharacteristics: For hot-dip galvanizing, a thin Zn coating (50-80 microns) is specified.Domex® MC grade steels conform to the provisions of EN 10149-2 standard and often have better properties.Property data is for hot-rolled steel..Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. General use of Domex® high strength steels offers a number of benefits compared to ordinary structural steels: Lower weight, Simpler production, Lower creep rate, Longer useful life, Higher load-bearing capacity, Lower transport costs, Reduced stocks, Lower overall cost.Data provided by SSAB Tunnplat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | Estimated by MatWeb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 430 - 550 MPa | 62400 - 79800 psi | |
| Tensile Strength, Yield | >= 355 MPa | >= 51500 psi | |
| Elongation at Break | >= 19 % @Thickness <=3.00 mm |
>= 19 % @Thickness <=0.118 in |
A<sub>80</sub> |
| >= 23 % @Thickness >=3.00 mm |
>= 23 % @Thickness >=0.118 in |
A<sub>5</sub> | |
| Impact | 133 | 133 | J/cm²; -20°C |
| 99.0 @Temperature -40.0 °C |
99.0 @Temperature -40.0 °F |
J/cm² | |
| Bend Radius, Minimum | >= 0.25 t | >= 0.25 t | t<3mm; internal bend radius, 90° |
| >= 0.50 t | >= 0.50 t | 3 mm < t< 6mm; internal bend radius, 90° | |
| >= 0.80 t | >= 0.80 t | t>6mm; internal bend radius, 90° |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | >= 0.015 % | >= 0.015 % | |
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Iron, Fe | 98 % | 98 % | As remainder |
| Manganese, Mn | <= 1.5 % | <= 1.5 % | |
| Niobium, Nb (Columbium, Cb) | <= 0.090 % | <= 0.090 % | |
| Phosphorous, P | <= 0.025 % | <= 0.025 % | |
| Silicon, Si | <= 0.030 % | <= 0.030 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | <= 0.15 % | <= 0.15 % | |
| Vanadium, V | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Polikim ULPOLEN® 1000 UHMWPE, Flame Retardant
- Aardvark Polymers AARTEL® 820UV Acetal Copolymer Rotational Molding Resin
- Techmer ES Plaslube® AC-81/TF/15 NAT Acetal (POM) Homopolymer
- Teijin Panlite® LN-1010RM High Light Reflection, Flame Resistant Polycarbonate Resin
- Diamond Polymers Centrex® 885 Profile Extrusion Grade
- Braskem EB 861/51 LDPE Blown Film Extrusion Polyethylene
- Teknor Apex APEX® 6500-70 Polyvinyl Chloride, Flexible
- Total Lumicene® mPE BM359 SG Metallocene Medium Density High Gloss Blow Molding Resin
- G-2712 Styrene-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved