SPS Guang Zhou POPTREEâ„¢ 6001 Flame-retarded Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE |
| Manufacturer | SPS Guang Zhou |
| Trade Name | POPTREE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SPS Guang Zhou POPTREEâ„¢ 6001 Flame-retarded Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristic: Low density, superior melt flow index, high notched impact strengthApplications: X'mas decorative productInformation Provided by SPS (Guang Zhou) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Melt Flow | 60 g/10 min | 60 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D638 |
| Flexural Strength | 6.00 MPa | 870 psi | |
| Flexural Modulus | 0.300 GPa | 43.5 ksi | |
| Izod Impact, Notched | 3.50 J/cm | 6.56 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 57.0 °C | 135 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 |
Users viewing this material also viewed the following:
- Hyosung Topilene R701 PP
- Industeel SUPERELSO® 500HR Quenched and Tempered High Strength Steel for Wet H2S Service
- Shakespeare FL-8 Fluorocarbon PVDF Fishing Line, 8 lb
- Plastics Group Polifil® RMT-40 40% Talc-Reinforced Polypropylene, High Impact
- Zeon Chemicals Nipol® 1034-60 Nitrile Elastomer
- Hexcel® Fibrelam® Grade 15 Panels for Aircraft Flooring
- Diamond Polymers NPP25-0604 Impact Copolymer Polypropylene
- CIMBAR Miti-Wite B3 Chemically Purified White Barite (BaSO4)
- Arkema Group LOTADER® 4720 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
Copyright © lookpolymers.com All Rights Reserved