- SCG Chemicals EL-Leneâ„¢ H1000P High Density Polyethylene Pipe Resin
SCG Chemicals EL-Leneâ„¢ H1000P High Density Polyethylene Pipe Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ H1000P High Density Polyethylene Pipe Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics: Good processing, high thermal stabilityRecommended Applications: Water pipes, conduit, sewage drainage pipesInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ISO 1183 |
| Environmental Stress Crack Resistance | >= 10000 hour | >= 10000 hour | F0; ASTM D1693 |
| Oxidative Induction Time (OIT) | >= 40 min @Temperature 200 °C |
>= 40 min @Temperature 392 °F |
ISO/TR10837 |
| Melt Flow | 0.22 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.22 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength at Break | 37.0 MPa | 5370 psi | Crosshead speed 100 mm/min; ISO 527 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | Crosshead speed 100 mm/min; ISO 527 |
| Elongation at Break | 823 % | 823 % | Crosshead speed 100 mm/min; ISO 527 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 3.04 J/cm @Temperature -20.0 °C |
5.69 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| 3.43 J/cm @Temperature 0.000 °C |
6.43 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 3.92 J/cm @Temperature 23.0 °C |
7.35 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Hydrostatic Design Basis | 10.0 MPa | 1450 psi | MRS Classified; ISO 9080 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S50R Silicone Rubber
- Polymer Resources TP-M30 Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced Warpage
- Malvern Minerals Sliastic 740 with 33% Novacite® L-207A Quartz Filler
- Teknor Apex Monprene® MP-1274G Thermoplastic Elastomer
- A. Schulman PP 1692 Polypropylene High Impact Copolymer
- Aclo Accutech Polypropylene Homopolymer HP0334T20L Talc Reinforced
- AIM 80In/Pb15/Ag5 Solder for Photonic Packaging
- ATI Allegheny Ludlum AL 29-4® Superferritic Stainless Steel, UNS S44700
- Beijing Evergrow Resources UHF-R3200 UHMW PE Fiber
- Buckeye Polymers BP RPP 1010 TR Blk Reprocessed Polypropylene, 10% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved