SABIC Innovative Plastics Xenoy® 1103 PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 1103 PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AUTOMOTIVE. Unreinforced, impact modified PBT+PC alloy. Excellent low temperature impact and chemical resistance. Range gray, black colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 250 °C |
13 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 150 % | 150 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.89 GPa | 274 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 77.0 MPa | 11200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.93 GPa | 280 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 61.0 J @Temperature 23.0 °C |
45.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 171 µm/m-°C @Temperature -40.0 - 40.0 °C |
95.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 200 µm/m-°C @Temperature -40.0 - 40.0 °C |
111 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 125 °C | 257 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Zircar Zirconia Buster M-35 Alumina Board, Disc, and Cylinder Insulation
- A. Schulman FORMION™ FI 401 Ionomer
- A. Schulman POLYFLAM™ RPP 1021 General Purpose Copolymer Polypropylene
- ConocoPhillips Hydroclear® 580 Industrial Oil
- 3M FA112 Destructible Acetate Label Products
- 3M Scotch-Weld™ 2262 Plastic Adhesive
- ExxonMobil Escorene® LD-728 High EVA Resin (discontinued **)
- Spartech Royalite R12 ABS General Purpose Sheet
- Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved