SABIC Innovative Plastics Valox® VIC4311 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® VIC4311 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm |
0.0060 - 0.0080 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | SABIC - Japan Method |
| Elongation at Break | 5.0 % | 5.0 % | SABIC - Japan Method |
| Flexural Strength | 128 MPa | 18600 psi | ASTM D790 |
| Flexural Modulus | 6.08 GPa | 882 ksi | ASTM D790 |
| Izod Impact, Notched | 1.37 J/cm | 2.57 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 50.0 - 60.0 Hz |
3.0 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- SABIC 518N Linear Low Density Polyethylene for Blown Film
- Chevron Phillips EB6025 HIPS - High Impact Polystyrene (discontinued **)
- Samyang Triloy® 230NH PC/ABS alloy, Flame Retardant
- Solvay ALKAMULS® OR 36 Surfactant
- Solvay RHODASURF® LA-9 Surfactant
- Lubrizol Pellethane® 2363-75D Thermoplastic Polyurethane Elastomer
- Trelleborg AEM Eccospheres® SID-311Z Sodium Borosilicate Glass Microspheres
- Trelleborg Emerson & Cuming Eccobond® TP 50 Two-Component Low Temperature Performance Silicone Adhesive
- Addiplast Addilene J 420 K24 Polypropylene Copolymer
- Asahi Kasei Leona® 1402F Nylon 66
Copyright © lookpolymers.com All Rights Reserved