SABIC Innovative Plastics Valox® V2105U PBT (Asia Pacific)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Valox®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Valox® V2105U PBT (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.

Physical Properties	Metric	English	Comments
Specific Gravity	1.28 g/cc	1.28 g/cc	ASTM D792
Density	1.28 g/cc	0.0462 lb/in³	ISO 1183
Moisture Absorption	0.0800 %	0.0800 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.34 %	0.34 %	ISO 62
Linear Mold Shrinkage, Flow	0.029 - 0.034 cm/cm @Thickness 3.20 mm	0.029 - 0.034 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.025 - 0.030 cm/cm @Thickness 3.20 mm	0.025 - 0.030 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	9.5 g/10 min @Load 5.00 kg, Temperature 266 °C	9.5 g/10 min @Load 11.0 lb, Temperature 511 °F	ASTM D1238
Melt Index of Compound	8.0 g/10 min @Load 5.00 kg, Temperature 265 °C	8.0 g/10 min @Load 11.0 lb, Temperature 509 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	52.0 MPa	7540 psi	50 mm/min; ISO 527
	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield	39.0 MPa	5660 psi	Type I, 50 mm/min; ASTM D638
	40.0 MPa	5800 psi	50 mm/min; ISO 527
Elongation at Break	230 %	230 %	50 mm/min; ISO 527
	300 %	300 %	Type I, 50 mm/min; ASTM D638
Elongation at Yield	6.0 %	6.0 %	50 mm/min; ISO 527
	17 %	17 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.50 GPa	363 ksi	5 mm/min; ASTM D638
	2.54 GPa	368 ksi	1 mm/min; ISO 527
Flexural Yield Strength	62.0 MPa	8990 psi	2 mm/min; ISO 178
	65.0 MPa	9430 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	1.87 GPa	271 ksi	2 mm/min; ISO 178
	2.06 GPa	299 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	11.6 J/cm	21.7 ft-lb/in	ASTM D256
	1.50 J/cm @Temperature -30.0 °C	2.81 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	98.0 kJ/m²	46.6 ft-lb/in²	80104; ISO 180/1A
	15.0 kJ/m² @Temperature -30.0 °C	7.14 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Charpy Impact, Notched	9.00 J/cm²	42.8 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	63.0 J @Temperature 23.0 °C	46.5 ft-lb @Temperature 73.4 °F	ASTM D3763
	75.0 J @Temperature -40.0 °C	55.3 ft-lb @Temperature -40.0 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	80.0 µm/m-°C @Temperature -40.0 - 40.0 °C	44.4 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	80.0 µm/m-°C @Temperature -40.0 - 40.0 °C	44.4 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	120 µm/m-°C @Temperature -40.0 - 40.0 °C	66.7 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	120 µm/m-°C @Temperature -40.0 - 40.0 °C	66.7 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	47.0 °C	117 °F	Flatw 80104 sp=64mm; ISO 75/Af
	49.0 °C @Thickness 3.20 mm	120 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	158 °C	316 °F	Rate B/50; ASTM D1525
	158 °C	316 °F	Rate B/50; ISO 306
	158 °C	316 °F	Rate B/120; ISO 306