SABIC Innovative Plastics Valox® TS4016 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® TS4016 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D 792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| 0.0070 - 0.0090 cm/cm @Thickness 6.40 mm |
0.0070 - 0.0090 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D 785 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | SABIC - Japan Method |
| Elongation at Break | 5.0 % | 5.0 % | SABIC - Japan Method |
| Flexural Strength | 104 MPa | 15100 psi | ASTM D 790 |
| Flexural Modulus | 4.21 GPa | 611 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.390 J/cm @Temperature 23.0 °C |
0.731 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 189 °C @Thickness 3.20 mm |
372 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH T2020 Polypropylene Homopolymer, Mineral Reinforced
- DSM Akulon® Ultraflow™ K-FHGM24 Nylon 6-30% Glass and Mineral Reinforced (European Grade) (Dry) (discontinued
- Hyosung Topilene J440F PP
- Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Shakespeare WP-200 diameter 0.2 mm Weft Polyester Monofilament
- Dow DOWLEX™ 2247G Polyethylene Resin
- Dow Engage® 8450 Polyolefin Elastomer
- Fainplast Compounds GS 7325 Flexible PVC, Injection Molding for Technical Items
- 3M 8067 All Weather Flashing Tape
- E-Polymers SEPAZ® N3040HR Nanoclay 3% Dimensional stability, Super Toughness Nano Composite Resin
Copyright © lookpolymers.com All Rights Reserved