SABIC Innovative Plastics Valox® SLWM2105 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® SLWM2105 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Anti-static PBT/PC blend, mineral 5% filled productThis data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.015 - 0.018 cm/cm @Thickness 3.20 mm |
0.015 - 0.018 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 30 g/10 min @Load 1.20 kg, Temperature 250 °C |
30 g/10 min @Load 2.65 lb, Temperature 482 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 20 % | 20 % | Type I, 10 mm/min; SABIC - Japan Method |
| Elongation at Yield | 20 % | 20 % | Type I, 10 mm/min; SABIC - Japan Method |
| Tensile Modulus | 2.42 GPa | 351 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 77.0 MPa | 11200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.410 J/cm @Temperature 23.0 °C |
0.768 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8980 (499) (UF) Synthetic Oil
- SABIC Innovative Plastics Cycoloy® C7240P PC+ABS (Asia Pacific)
- Spartech M60095 General Purpose PVC
- Styron EMERGEâ„¢ 7700 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)
- Formosa Plastics Formolene® HB5502F Blow Molding HDPE
- Aclo Accutech Polypropylene Homopolymer HP0339G15M15CL Glass/Mineral Reinforced Coupled
- Applied Composites 8079 Modified Vinylester SMC
- 3M FMV22 Void Polyester Label Products
- SABIC Innovative Plastics LNP Thermocomp TX88477 PU
- Schmolz + Bickenbach Formadur® 2311 Plastic Mold Steel
Copyright © lookpolymers.com All Rights Reserved