SABIC Innovative Plastics PREVEX W20 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Prevex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics PREVEX W20 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive. PPE alloy. High flow/impact. Instrument panels and interior trim components. HDT 210F.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 52 % | 52 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.93 GPa | 280 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.03 GPa | 294 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 3.47 J/cm | 6.50 ft-lb/in | ASTM D256 |
| 2.13 J/cm @Temperature -30.0 °C |
3.99 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Gardner Impact | 37.0 J | 27.3 ft-lb | ASTM D3029 |
| 27.0 J @Temperature -40.0 °C |
19.9 ft-lb @Temperature -40.0 °F |
ASTM D3029 | |
| 29.0 J @Temperature -30.0 °C |
21.4 ft-lb @Temperature -22.0 °F |
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 103 °C @Thickness 6.40 mm |
217 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs AG100 AgC2H3O2 Silver acetate
- SABIC Innovative Plastics Lexan® 241R PC (Europe-Africa-Middle East)
- ExxonMobil Dytron™ XK7300-92 Thermoplastic Elastomer (discontinued **)
- Momentive Performance Materials HV 3/806 Heat Cured Rubber - High Temperature
- Eifeler Coatings Technology MoST™ Molybdenum disulfide PVD Coating
- Crucible Steel JIS SUH600 Martensitic Steel
- California Fine Wire Nico Copper Nickel Resistance Wire
- Azoty Tarnow™ Tarnamid® T-27 GF35 Polyamide 6 - Glass Fiber Reinforced
- Axiall 19890 Wire & Cable Flexible PVC
- Weartech International WT-1 Cobalt Hardfacing & Wear Resistant Alloy
Copyright © lookpolymers.com All Rights Reserved