PolyOne Geon™ 170 Series Adept E 49 Polyvinyl Chloride Homopolymer (PVC Homopolymer)

Category	Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer	PolyOne Corporation
Trade Name	Geon™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Geon™ 170 Series Adept E 49 Polyvinyl Chloride Homopolymer (PVC Homopolymer).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Geon® Adept E49 is a low molecular weight homopolymer dispersion resins intended for use in variety of plastisol applications and processes. It reduces scrap rates and manufacturing costs by extending plastisol shelf life with reduced viscosity aging performance. It improves non settling characteristic in hot melt system. Geon® Adept E49 is recommended for solid plastisol applications for instance the hard and soft products produced from hot melt plastisols, high clarity and gloss textile screen (printing) inks.Note: The value set forth represent typical values and PolyOne Corporation, therefore, makes no representation that the material in any particular shipment will conform to the listed properties. Packaging: This resin is shipped in multi-wall paper bags, net weight 50 lbs, 2500 lbs per pallet. Information shown on the package includes commercial identification number, lot and weight. Geon® ALTC and ASTM D638 (formulation): 100phr Geon® Adept E 49, 57phr DINP, 3phr ESO, and 2phr Therm-Chek SP 120 LOHF Geon® STP 390(formulation): 100phr Geon® Adept E 49, and 60phr DOPInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.40 g/cc	1.40 g/cc	ASTM D792
Bulk Density	0.272 g/cc	0.00983 lb/in³
Fineness	5.0	5.0	Hegman, North Fineness; Geon® 390
Relative Viscosity	2.12 cP	2.12 cP	Correlation, Cyclohexanone 1%; Internal Method
Brookfield Viscosity	2.65 cP	2.65 cP	Initial Viscosity @ 20 rpmGeon® ALTC 22 (with provided formulation); Internal Method
	3.35 cP	3.35 cP	One Day Viscosity @ 20 rpmGeon® ALTC 22 (with provided formulation); Internal Method
	3.85 cP	3.85 cP	Initial Viscosity @ 2 rpmGeon® ALTC 22 (with provided formulation); Internal Method
	4.95 cP	4.95 cP	One Day Viscosity @ 2 rpmGeon® ALTC 22 (with provided formulation); Internal Method
Viscosity Measurement	0.85	0.85	Inherent; ASTM D1243-60-A
Melt Flow	120 g/10 min @Pressure 0.655 MPa	120 g/10 min @Pressure 95.0 psi	Severs Efflux; Geon® ALTC 23 (with provided formulation); Internal Method

Mechanical Properties	Metric	English	Comments
Tensile Strength	10.7 MPa	1550 psi	Optimum; With provided formulation; ASTM D638

Optical Properties	Metric	English	Comments
Gloss	90 %	90 %	60 Degree Fused 5 mins @ 350FGeon® ALTC 65 (with provided formulation); Internal Method
Transmission, Visible	97 %	97 %	Geon® ALTC 66 (with provided formulation); Internal Method

Processing Properties	Metric	English	Comments
Moisture Content	0.090 %	0.090 %	Karl FisherGeon® STP 683; Internal Method

Descriptive Properties	Value	Comments
Features	High Clarity
	High Gloss
Forms	Powder	Fine, white powder
Gel Temperature	71 °C	Internal Method; Geon® ALTC 29 (with provided formulation)
Generic Material	PVC Homopolymer
Generic Name	Polyvinyl Chloride Homopolymer (PVC Homopolymer)
K-Value	64	Internal Method; Correlation, (0.5gm/100ml)
Methanol Extractables	1.3%	Internal Method; Geon® STP 894
Polymerization Process	Emulsion
Processing Method	Dip Coating
	Hot Melt
	Ink Jet Digital Printing
	Rotational Molding
	Slush Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Residual Vinyl Chloride Monomer	< 9 ppm	Internal Method; Geon® STP 1005