SABIC Innovative Plastics NORYL PX2949 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX2949 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS GF+Mineral Filler total 40%
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
SABIC Method |
| 0.0025 cm/cm @Thickness 6.40 mm |
0.0025 in/in @Thickness 0.252 in |
SABIC Method | |
| Melt Flow | 22 g/10 min @Load 10.0 kg, Temperature 250 °C |
22 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 92.0 MPa | 13300 psi | SABIC - Japan Method |
| Elongation at Break | 7.0 % | 7.0 % | SABIC - Japan Method |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 9.72 GPa | 1410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 - 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.7 - 29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C @Thickness 6.40 mm |
255 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | 5VA @Thickness 2.80 mm |
5VA @Thickness 0.110 in |
UL 94 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® CP 1319
- Hong Kun Group 3-Chloro-2-fluorobenzaldehyde Pharmaceutical Intermediate
- Huntsman AVALON® 65 AC Thermoplastic Polyurethane
- Techmer ES HiFill FR® PP CO FR-N V2
- Zeon Chemicals Zeonor® 750R Cyclo Olefin Polymer
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 2.0 PHR Di-Cup 40C
- Eagle Brass 425 Tin Brass 2%, Hard
- DuPont Performance Polymers Crastin® S600F20UV WT660 Polybutylene Terephthalate (PBT)
- DuPont Teijin Films Melinex® 377 Polyester Film, 500 Gauge
Copyright © lookpolymers.com All Rights Reserved