SABIC Innovative Plastics NORYL PVX516 PPE
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PVX516 PPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PREVEX* PVX516 resin is a high flow, non FR grade, 110 C HDT
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption at Saturation | 0.070 % | 0.070 % | ISO 62 |
| Viscosity | 145000 cP | 145000 cP | Melt Viscosity, 280°C, 1500 sec-1; ISO 11443 |
| Melt Index of Compound | 16 g/10 min @Load 5.00 kg, Temperature 280 °C |
16 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 |
| 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 23 % | 23 % | Type I, 50 mm/min; ASTM D638 |
| 28 % | 28 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 2.4 % | 2.4 % | 50 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.42 GPa | 351 ksi | 1 mm/min; ISO 527 |
| 2.47 GPa | 358 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.36 GPa | 342 ksi | 2 mm/min; ISO 178 |
| 2.54 GPa | 368 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.20 J/cm | 4.12 ft-lb/in | ASTM D256 |
| 0.990 J/cm @Temperature -30.0 °C |
1.85 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact Unnotched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 12.0 J @Temperature -40.0 °C |
8.85 ft-lb @Temperature -40.0 °F |
ASTM D3763 |
| 24.0 J @Temperature 23.0 °C |
17.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 124 °C | 255 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® SLX2431D PC Copolymer
- SABIC Innovative Plastics LNP STAT-KON DEP23FXC PC
- Teknor Apex Telcar® TL-83-F912-UV Thermoplastic Elastomer
- E-Polymers TEKANATE® G7020 General Purpose Easy Molding Polycarbonate
- BASF Neopolen® P 9230 K 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- Azoty Tarnow™ Tarnamid® T-27 MF30 Polyamide 6 - Mineral Reinforced
- ConocoPhillips Conoco® El Mar® Grade 40 Mid Ash Supreme Oil
- DuPont™ Sclairfilm® LWS-1 LMDPE Film, Laminating, 38.1 µm Thickness (discontinued **)
Copyright © lookpolymers.com All Rights Reserved