SABIC Innovative Plastics NORYL GTX APS440 PPE+PPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX APS440 PPE+PPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PPS, GF40%, FR V-0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 46.6 g/10 min @Load 5.00 kg, Temperature 300 °C |
46.6 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 127 MPa | 18400 psi | SABIC - Japan Method |
| Elongation at Break | 7.0 % | 7.0 % | SABIC - Japan Method |
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| Flexural Modulus | 10.78 GPa | 1564 ksi | ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 - 58.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.0 - 32.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C @Thickness 6.40 mm |
495 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.6 @Frequency 50.0 - 60.0 Hz |
3.6 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PPE 1462 (discontinued **)
- LG Chemical PB1752 PVC
- KKPC Kuhmo HF401 Flame Retarded General Purpose HIPS
- Kuraray SEPTON® CM1 Compatibilizer
- Shin-Etsu Silicones SV-56000U High Strength Silicone Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP RX00713H PA 66
- Solvay RHODAPHOSE® BIS DIPHENYL PHOSPHINO ETHANE Phosphorus Derivative
- Unitika AX-1500 Dry
- Fainplast Compounds Hax™ HFX 507 Crosslinkable HFFR Cable Compound
- 3M Nextel™ AP-18 Woven Tape 312 (2.5 cm)
Copyright © lookpolymers.com All Rights Reserved