SABIC Innovative Plastics Lexan® NX07331 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® NX07331 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FARADEX NX07331 is a commercial grade EMI shielding material
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.40 g/cc | 0.0470 - 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption | <= 0.0800 % | <= 0.0800 % | 23°C / 50% RH; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 40.0 MPa | >= 5800 psi | UL 1581 |
| Tensile Modulus | >= 3.80 GPa | >= 551 ksi | 5 mm/min; ASTM D638 |
| Flexural Modulus | >= 3.40 GPa | >= 493 ksi | 6.4 mm; ASTM D790 |
| Izod Impact, Notched (ISO) | >= 100 kJ/m² | >= 47.6 ft-lb/in² | 80*10*3; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | >= 500 kJ/m² | >= 238 ft-lb/in² | 80*10*3; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 120 °C @Thickness 6.40 mm |
>= 248 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness <=1.80 mm |
HB @Thickness <=0.0709 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Shielding Effectiveness | >= 40 dB @Thickness 3.00 mm |
>= 40 dB @Thickness 0.118 in |
SABIC Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Melt Flow Rate, 270°C/10 kgf | Y10 - 20g/10 min | ASTM D1238 |
| Surface Resistivity | Y1.E+04 - 1.E+06Ohm | ASTM D257 |
| Tensile Strain, break, 50 mm/min | Y2 - 3.6% | ISO 527 |
Users viewing this material also viewed the following:
- RheTech Products G40P100-00 40% Glass Fiber Reinforced Polypropylene, Natural
- PEAK Werkstoff DISPAL S693 Aluminum Alloy, AlCu5Ti, Condition T6
- Resin Technology Group UV-406 High Clarity, Moisture Resistant, UV Curing Bonder
- Lucent Polymers GPB-130 Polybutylene Terephthalate, 30% Glass Fiber Reinforced
- Lehmann & Voss LUVOCOM® 1301-0825 PPS, linear, with carbon fiber
- A. Schulman POLYFLAM™ RPP 1058 General Purpose Homopolymer Polypropylene (30% Fiberglass)
- Cossa Polimeri ESTACARB 1001 Polycarbonate
- EPICHEM Epilon G2-PC 10% GF Polycarbonate, 10% Glass Fiber
- Colorite Polymers 9234 General Purpose Vinyl Compound
- LNP ULTEM® SMU5852 Polyetherimide, 30% Carbon Fiber Reinforcement, 15% PTFE Lubricant (discontinued **)
Copyright © lookpolymers.com All Rights Reserved