SABIC Innovative Plastics Lexan® ML6451 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® ML6451 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UV-stabilized, co-extrusion capstock material. Minimal processing values available at this time.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Melt Flow | 10.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
10.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 98 % | 98 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 104 MPa | 15100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.59 GPa | 376 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C @Thickness 3.20 mm |
237 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- LNP Emi-X® OC-1008 LEX Polyphenylene Sulfide, Carbon Fiber Reinforcement (discontinued **)
- Lehmann & Voss LUVOCOM® 1106-8124 Polyether imide, lubricant modified
- MetalTek MTEK CY-40 Cast UNS N06040 Severe Corrosion and Heat Resistant Alloy
- Sylvin Technologies 8940-95 Natural PVC Extrusion Compound
- Taiwan Sheen Soon Sheenthane® A9030 Thermoplastic Polyurethane Elastomer
- Master Bond EP13 High Temperature Resistant One Component Epoxy System
- 3M Scotchcal™ 3632-156 Translucent Film
- 3M Scotch-Weld™ 1357 Neoprene High Performance Contact Adhesive
- A. Schulman ComAlloy Hiloy® 512 Polycarbonate, Glass Reinforced, UL
- BorsodChem ONGROVIL S-5070 Suspension PVC-Resin
Copyright © lookpolymers.com All Rights Reserved