Arkema Group Rilsan® BZM 8 NOIR TL Nylon 11, 8% Glass Fiber Filled (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with 10% Glass Fiber Filler
Manufacturer	Arkema
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® BZM 8 NOIR TL Nylon 11, 8% Glass Fiber Filled (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation ISO 1874-PA11,MHL,18-020,GF8Rigid grade with glass fiber (8%) filler for injection molding. Available color: black. Light and heat stabilized.Rigidity. Outstanding compromise between good impact strength and rigidity. Low linear expansion coefficient. Low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability.UL classification: UL94 HB RTI(C) 65/65/65Example applications: Sport parts.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Melt Flow	4.5 g/10 min @Load 2.16 kg, Temperature 235 °C	4.5 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	68.0 MPa	9860 psi	50 mm/min
Elongation at Break	15 %	15 %	Nominal Strain; 50 mm/min
Elongation at Yield	4.0 %	4.0 %	50 mm/min
Tensile Modulus	3.32 GPa	482 ksi	1 mm/min
Charpy Impact Unnotched	8.50 J/cm²	40.5 ft-lb/in²
	9.17 J/cm² @Temperature -30.0 °C	43.6 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	1.06 J/cm²	5.04 ft-lb/in²
	0.550 J/cm² @Temperature -30.0 °C	2.62 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	65.0 µm/m-°C @Temperature 20.0 °C	36.1 µin/in-°F @Temperature 68.0 °F