Mapal Plastics Maplon Type O Polypropylene Sheet
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade |
| Manufacturer | Mapal Plastics |
| Trade Name | Maplon |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mapal Plastics Maplon Type O Polypropylene Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties: Corona treated on both sides for offset and screen printing, Extended shelf life, Low stress whitening, Suitable for die cuttingApplications: Stationery products, Offset printed item
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | |
| Thickness | 1000 microns | 39.4 mil | |
| Surface Tension | >= 48 dynes/cm | >= 48 dynes/cm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 26.0 MPa @Temperature 23.0 °C |
3770 psi @Temperature 73.4 °F |
ASTM D638 |
| Film Tensile Strength at Yield, TD | 23.0 MPa @Temperature 23.0 °C |
3340 psi @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Break, MD | >= 650 % @Temperature 23.0 °C |
>= 650 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Break, TD | >= 300 % @Temperature 23.0 °C |
>= 300 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Yield, MD | 23 % @Temperature 23.0 °C |
23 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Yield, TD | 19 % @Temperature 23.0 °C |
19 % @Temperature 73.4 °F |
ASTM D638 |
| Modulus of Elasticity | 0.300 GPa @Temperature 23.0 °C |
43.5 ksi @Temperature 73.4 °F |
MD/TD; ASTM D638 |
| Izod Impact, Notched | 1.00 J/cm @Thickness 3.20 mm, Temperature 0.000 °C |
1.87 ft-lb/in @Thickness 0.126 in, Temperature 32.0 °F |
ASTM D256 |
| 4.20 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
7.87 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 5.50 J @Temperature 23.0 °C |
4.06 ft-lb @Temperature 73.4 °F |
ASTM D1709-85 |
| Dart Drop Total Energy | 55.0 J/cm @Temperature 23.0 °C |
0.103 ft-lb/mil @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 140 °C | 284 °F | ASTM D1525 |
| Heat Distortion Temperature | 80.0 °C | 176 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Mapal Color Catalogue No. 520002 |
Users viewing this material also viewed the following:
- Huntsman Araldite GT 7013 Bisphenol A Epoxy Solid Resin
- LG Chemical SEETEC ST508 Linear Low Density Polyethylene, Cast Film Grade
- Samyang Tribit® 1500G15 Polybutylene Terephthalate, 15% Glass Reinforced
- A. Schulman POLYFORT™ PP 1329 Medium Impact Copolymer Polypropylene
- A. Schulman POLYFORT™ PP 3726
- A. Schulman POLYBATCH™ Treated Pine 60175U/4 Concentrate Based In LLDPE
- Dow C702-20 Polypropylene Impact Copolymer Resin
- Colorite Polymers 91-477 General Purpose Vinyl Compound
- 3M FV065 Semi-Rigid White Vinyl Label Product
Copyright © lookpolymers.com All Rights Reserved