SABIC Innovative Plastics LNP VERTON RX06422 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RX06422 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* RX06422 is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm @Time 86400 sec |
0.0018 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0018 cm/cm @Time 86400 sec |
0.0018 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0022 cm/cm @Time 86400 sec |
0.0022 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0022 cm/cm @Time 86400 sec |
0.0022 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 254 MPa | 36800 psi | ASTM D638 |
| 265 MPa | 38400 psi | ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| 1.9 % | 1.9 % | ISO 527 | |
| Tensile Modulus | 16.89 GPa | 2450 ksi | 50 mm/min; ASTM D638 |
| 18.38 GPa | 2666 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 370 MPa | 53700 psi | ISO 178 |
| 374 MPa | 54200 psi | ASTM D790 | |
| Flexural Modulus | 14.16 GPa | 2054 ksi | ASTM D790 |
| 15.55 GPa | 2255 ksi | ISO 178 | |
| Izod Impact, Notched | 3.84 J/cm | 7.19 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| 38.0 kJ/m² @Temperature -40.0 °C |
18.1 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 89.0 kJ/m² | 42.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 15.0 J | 11.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 18.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 67.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 67.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 241 °C @Thickness 3.20 mm |
466 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nitriflex NitriClean 2858 NBR - Nitrile Rubber
- Resinlab® UR3001HP Black Urethane Encapsulant
- 3M Dyneon™ PFA 6503 C EPC Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- Sibur ABS 1530 Molding Grade ABS Plastic
- Teknor Apex Elexar® EL 3954-62 Thermoplastic Elastomer
- SABIC Innovative Plastics Noryl GTX GTX966 PPE+PA66 (Asia Pacific)
- Lubrizol Stat-Rite® X-5076 Static Control High Impact Polystyrene
- A. Schulman ComAlloy® E-14756 Flame Retardant Easy Flow Polycarbonate Alloy
- Hexcel® HexForce™ 130 Carbon Fabric
- Resirene Resirene® HF-555 General Purpose Polystyrene
Copyright © lookpolymers.com All Rights Reserved