SABIC Innovative Plastics LNP VERTON RVN17SXS PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RVN17SXS PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RVN17SXS is a compound based on PA 66 resin containing Long Glass Fiber, MoS2. Added features include; Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 1.0 % @Time 86400 sec |
1.0 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0044 cm/cm @Time 86400 sec |
0.0044 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.6 GPa | 1830 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 263 MPa | 38100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.2 GPa | 1480 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.25 | 0.25 | ASTM D3702 Modified |
| K (wear) Factor | 80.6 x 10-8 mm³/N-M | 40.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 264 °C | 507 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy 132 Tin Solder Alloy
- Samsung Cheil Industries Starex® LX-0987EXS ABS, Unreinforced Metallic-Look
- Polyplastics FR-PET® CN9030 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose
- Hexcel® HexPly® M48 180°C/356°F Curing Epoxy Matrix, M48/42%/G1094/1000
- Aclo Accutech Polypropylene Homopolymer HP0336C30L Calcium Reinforced
- BASF Novolen® 1100 L Polypropylene, Injection Molding Grade
- Asahi Kasei Thermofil P-30TC-1156 30% Talc Filled, Heat Stabilized
- Amity Thermosets ATM 144 Phenolic Molding Organic Filler, Compression Molded
- Permabond HM135 Anaerobic Retainer
- Compuestos Dominicanos Polycom CH-550140 PVC Compound
Copyright © lookpolymers.com All Rights Reserved