SABIC Innovative Plastics LNP Thermocomp ZM3242 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp ZM3242 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified PPO* 30% mineral filled products, Non Halogenated Flame Retardant V-1 products.Supper low warpage series, HDT 110degCThis data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.00 % | 0.00 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.00 % @Temperature 23.0 °C |
0.00 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 300 °C |
27 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 104 MPa | 15100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 5.77 GPa | 837 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.230 J/cm @Temperature 23.0 °C |
0.431 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- RheTech Products T28P100-01EG 28% Talc Reinforced Polypropylene, Black, Extrusion Grade
- Ferro EG 2928 Glaze and Sealant Glass
- Solvay TECHNYL® C 216 V45 PA6, 45% glass fiber, DRY
- SABIC Innovative Plastics LNP THERMOCOMP BF006 SAN (Europe-Africa-Middle East)
- Solvay GEROPON® TC 42 LQ Surfactant
- Lubrizol ESTANE® 58300 Ether Based Thermoplastic Polyurethane (European Grade)
- Dow Corning SYL-OFF® 23-30% COATING
- DSM Novamid® ST220 NAT PA6-I
- Axion Polymers Axpoly® PS13 1011 High Impact Polystyrene
- SABIC Innovative Plastics LNP VERTON RV00ASXS PA 66 (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved