SABIC Innovative Plastics LNP Thermocomp YF006 TPEE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp YF006 TPEE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* YF006 is a compound based on TPEE resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| 1.441 g/cc | 0.05206 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.42 % | 0.42 % | 23°C / 50% RH; ISO 62 |
| 0.31 % @Time 86400 sec |
0.31 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0022 cm/cm @Time 86400 sec |
0.0022 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0075 cm/cm @Time 86400 sec |
0.0075 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | ASTM D 638 |
| 57.0 MPa | 8270 psi | ISO 527 | |
| Elongation at Break | 10.5 % | 10.5 % | ASTM D 638 |
| 10.5 % | 10.5 % | ISO 527 | |
| Tensile Modulus | 2.27 GPa | 329 ksi | 50 mm/min; ASTM D 638 |
| 3.07 GPa | 445 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 77.0 MPa | 11200 psi | ISO 178 |
| 79.0 MPa | 11500 psi | ASTM D 790 | |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D 790 |
| 3.09 GPa | 448 ksi | ISO 178 | |
| Izod Impact, Notched | 3.63 J/cm @Temperature 23.0 °C |
6.80 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 33.0 kJ/m² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 93.0 kJ/m² @Temperature 23.0 °C |
44.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 45.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 151 µm/m-°C @Temperature -40.0 - 40.0 °C |
83.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 152 µm/m-°C @Temperature -40.0 - 40.0 °C |
84.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 187 °C @Thickness 3.20 mm |
369 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 6042S
- Polykemi AB POLYfill PPH GF15020 PD1 NBR PP, Glass Fiber-Reinforced, Chemically Coupled
- PSM Industries Ferro-TiC® HT-6A Age Hardenable Nickel Base
- SABIC Innovative Plastics REMEX VR4831 PBT
- 3M Scotch Pad™ 8328 Custom Carry Handle
- ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367)
- 3M Dyneon™ FG 5661 Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved