- SABIC Innovative Plastics LNP Thermocomp PFB139E PA 6 (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP Thermocomp PFB139E PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp PFB139E PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PFB139E is a compound based on PA 6 resin containing Glass Fiber, Glass Bead, Flame Retardant. Added features include; Flame Retardant, Easy Molding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec |
1.3 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 121 MPa | 17500 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 121 MPa | 17500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 3.5 % | 3.5 % | Flexural Strain, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.80 GPa | 986 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 169 MPa | 24500 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 170 MPa | 24700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 97.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
53.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPC-10G Black Polypropylene Copolymer (PP Copolymer)
- Potters Industries Spheriglass® Spacer Bead Solid Soda-Lime Glass Spheres
- Polykemi AB POLYfill PPC T25020 UV Polypropylene Copolymer, Mineral Reinforced
- Mallard Creek Polymers Tykote® 6152 Styrene-Acrylic Emulsion
- Universal Wire Works 4047 (718) (AMS 4185) Aluminum Alloy Filler Metal
- Trelleborg S850 Silicone Rubber
- Hexcel® HexWeb® HRH-10 - 1/8- 6.0 Aramid Fiber/Phenolic Resin Honeycomb
- DSM Akulon® K222-KGV4 Nylon 6-20% Glass Reinforced (European and Asian Grade) (Cond)
Copyright © lookpolymers.com All Rights Reserved