SABIC Innovative Plastics LNP Thermocomp OFJ66 PPS - Linear (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp OFJ66 PPS - Linear (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OFJ66 is a compound based on PPS - Linear resin containing Glass Fiber, Mineral. Added features of this material include: Low Warpage.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.95 g/cc | 0.0704 lb/in³ | ISO 1183 |
| 1.96 g/cc | 0.0708 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.030 cm/cm @Time 86400 sec |
0.030 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| 134 MPa | 19400 psi | ASTM D 638 | |
| Elongation at Break | 1.2 % | 1.2 % | ASTM D 638 |
| 1.2 % | 1.2 % | ISO 527 | |
| Tensile Modulus | 19.0 GPa | 2760 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 199 MPa | 28900 psi | ASTM D 790 |
| 210 MPa | 30500 psi | ISO 178 | |
| Flexural Modulus | 18.8 GPa | 2730 ksi | ISO 178 |
| 19.21 GPa | 2786 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 19.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 24.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 30.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 265 °C @Thickness 3.20 mm |
509 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- SABIC Innovative Plastics Xenoy® IQ4840 PBT+PC (Europe-Africa-Middle East)
- Saint-Gobain CHR® M787 Polyester Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics NORYL GTX GTX8120P PPE+PA (Europe-Africa-Middle East)
- Styron PULSEâ„¢ EXT 200 PC/ABS Engineering Resin
- Teknor Apex Telcar® TL-1000-92-UV Thermoplastic Elastomer
- EMS-Grivory Grivory® LV-65H FWA nat PA12-GF65
- 3M 9019 Double Coated Tapes with Adhesive 300
- SABIC Innovative Plastics Ultem ATX103R PEI+PCE
Copyright © lookpolymers.com All Rights Reserved