SABIC Innovative Plastics LNP Thermocomp MX05039 PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MX05039 PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MX05039 is a compound based on Polypropylene resin containing Mineral, colorant. Added features include : Heat- Stabilized, UV - Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Water Absorption | 0.030 % @Temperature 23.0 °C, Time 86400 sec |
0.030 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.0 MPa | 2610 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.9 % | 3.9 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 36.0 MPa | 5220 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 105 µm/m-°C @Temperature 23.0 - 60.0 °C |
58.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 139 µm/m-°C @Temperature 23.0 - 60.0 °C |
77.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Polymax® Maxelast® F02-139A TPE, Halogen Free Extrusion Grade
- Kennametal Stellite Nistelle 2315 Nickel Superalloy
- Multibase Multi-Flex® A 4001 LC TPE Thermoplastic Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP KG002 Acetal Copolymer (Europe-Africa-Middle East)
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7360-9000 TPE
- Teknor Apex Monprene® MP 1079E Thermoplastic Elastomer
- Zeon Chemicals Quintac® 3421 SIS Block Polymer
- Eurostar Starpylen M1000-BK1A987 PP, Carbon Black
- Arkema Group ORGASOL® 2002 ES 4 Nat 3 Polyamide 12
- BASF Ultramid® 1000-2 NF2001 PA66 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved