SABIC Innovative Plastics LNP Thermocomp GX061104 PSU (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp GX061104 PSU (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* COLORCOMP* GX061104 is a compound based on Polysulfone resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 0.30 %

@Temperature 23.0 °C,
Time 86400 sec
 0.30 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
50 mm/min; ISO 527
Tensile Strength, Yield 73.0 MPa
10600 psi
50 mm/min; ISO 527
Elongation at Yield 5.9 %
5.9 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527
Flexural Yield Strength 113 MPa
16400 psi
2 mm/min; ISO 178
Flexural Modulus 2.60 GPa
377 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 151 °C
304 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af