SABIC Innovative Plastics LNP Thermocomp CF004 PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp CF004 PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* CF004 is a compound based on Polystyrene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.70 GPa | 972 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.30 GPa | 769 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
32.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE G 7890 BLK
- SABIC Innovative Plastics Lexan® HP2EU PC (Europe-Africa-Middle East)
- DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, Uncured Carbon Black Filled Compound &
- Lubrizol Advanced Materials Pearlthane® MB-51UV Thermoplastic Polyurethane Elastomer
- Solvay TECHNYLSTARâ„¢ SX 218 V60 Black Z PA6, 60% glass filled, Conditioned
- SABIC Innovative Plastics ULTEM 1010FC PEI (Europe-Africa-Middle East)
- Techmer ES HiFill® PA6/6 GF33 SL5 33% Glass Filled
- Samyang Trirex® 3000H Polycarbonate, Low-temperature Impact
- Chesterton OPTICOOL™ 572 Lubrication
- Elektro-Isola G-Etronax M Melamine, Glass Fabric Reinforcement, White, Sheets
Copyright © lookpolymers.com All Rights Reserved