SABIC Innovative Plastics LNP Thermocomp AF008 ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp AF008 ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* AF008 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 77.0 MPa | 11200 psi | ASTM D 638 |
| Elongation at Break | 0.90 % | 0.90 % | ASTM D 638 |
| Tensile Modulus | 11.99 GPa | 1739 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D 790 |
| Flexural Modulus | 10.16 GPa | 1474 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.23 J/cm @Temperature 23.0 °C |
4.18 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C @Thickness 3.20 mm |
216 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ CPVC EC050 Polyvinyl Chloride, Chlorinated (CPVC)
- Hong Kun Group HBTU Pharmaceutical Intermediate
- KB Alloys 3% Bismuth Aluminum Alloy
- H.C. Starck Grade HS Boron Carbide, B4C
- Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, Conditioned
- Wellman Wellamid® MRGF25/15 42H-NBK1 40% Mineral/Glass Fiber Reinforced Nylon 6
- EPICHEM Epinyl PA 66 GF 30 Polyamide 66, 30% Glass
- 3A Composites Core Materials AIREX® T92.100 Easy Processing Structural Foam
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved