SABIC Innovative Plastics LNP THERMOTUF DF008EI PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF DF008EI PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* DF008EI is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.00040 cm/cm @Time 86400 sec |
0.00040 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0033 cm/cm @Time 86400 sec |
0.0033 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527 |
| 132 MPa | 19100 psi | ASTM D638 | |
| Tensile Strength, Yield | 129 MPa | 18700 psi | ISO 527 |
| 132 MPa | 19100 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 11.06 GPa | 1604 ksi | 1 mm/min; ISO 527 |
| 12.63 GPa | 1832 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| 199 MPa | 28900 psi | ASTM D790 | |
| Flexural Modulus | 10.09 GPa | 1463 ksi | ISO 178 |
| 10.61 GPa | 1539 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.38 J/cm | 15.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 23.0 J | 17.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 26.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 42.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GTPO8290-GT7 PVC
- SABIC Innovative Plastics Lexan® EXL1433T PC Copolymer (Europe-Africa-Middle East)
- Raschig Group 3535 Epoxy
- Karina E 855-10/150-ERYB-PO White PVC Compound
- Ex-Tech Plastics RenewTech™ BioPlastics Ingeo™ PLA
- Fainplast Compounds EVAtech 801S Ethylene Vinyl Acetate Foam
- Axiall 8630 Moldings & Extrusions Flexible PVC
- Arlon 47568R055E 0.0075" Cured Silicone Rubber/Fiberglass/Acrylic PSA Laminate
- Buckeye Polymers BP RPP 1012 T BLK Polypropylene, Talc Filled
- BASF Methyl Chloroformate
Copyright © lookpolymers.com All Rights Reserved