SABIC Innovative Plastics LNP THERMOCOMP WF006 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WF006 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* WF006 is a compound based on PBT resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| 1.559 g/cc | 0.05632 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0107 cm/cm @Time 86400 sec |
0.0107 in/in @Time 24.0 hour |
ISO 294 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 133 MPa | 19300 psi | ISO 527 |
| 137 MPa | 19900 psi | ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| 2.9 % | 2.9 % | ASTM D638 | |
| Tensile Modulus | 10.16 GPa | 1474 ksi | 50 mm/min; ASTM D638 |
| 11.18 GPa | 1622 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 208 MPa | 30200 psi | ISO 178 |
| 222 MPa | 32200 psi | ASTM D790 | |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ISO 178 |
| 9.35 GPa | 1360 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.38 J/cm | 15.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 31.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Geloy HRA222 ASA (Europe-Africa-Middle East)
- PTS PCA-2201NHV Non Bromine, Non Chlorine Flame Retardant Polycarbonate/ABS Alloy, UV Stabilized
- PolyOne Geon™ Vinyl Flexible R328BE Polyvinyl Chloride, Flexible (PVC, Flexible)
- LTL Color Compounds ColorFast® ACR100IM Polymethylmethacrylate, High Impact
- Indium Corp. NanoFoil® NF40 Nickel and Aluminum Localized Heat Source For Bonding
- Solvay Specialty Polymers Veradel® 3500 Polyethersulfone (PESU)
- ExxonMobil Oppera PR 100A (AM) Modifier
- Axiall 7140 Rigid PVC, Extrusion & Molding
Copyright © lookpolymers.com All Rights Reserved