SABIC Innovative Plastics LNP THERMOCOMP TH0300A PUR
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP TH0300A PUR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* TH0300A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.999 g/cc | 0.1083 lb/in³ | ASTM D792 |
| 3.19 g/cc | 0.115 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.250 % | 0.250 % | 50% RH, 24 hrs; ASTM D570 |
| 0.390 % | 0.390 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0102 cm/cm @Time 86400 sec |
0.0102 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ASTM D638 |
| 28.0 MPa | 4060 psi | ISO 527 | |
| Elongation at Break | 225.9 % | 225.9 % | ASTM D638 |
| Elongation at Yield | 15 % | 15 % | ISO 527 |
| 53.3 % | 53.3 % | ASTM D638 | |
| Tensile Modulus | 0.230 GPa | 33.4 ksi | 50 mm/min; ASTM D638 |
| 0.390 GPa | 56.6 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 10.0 MPa | 1450 psi | ISO 178 |
| 12.0 MPa | 1740 psi | ASTM D790 | |
| Flexural Modulus | 0.330 GPa | 47.9 ksi | ASTM D790 |
| 0.400 GPa | 58.0 ksi | ISO 178 | |
| Izod Impact, Notched | 5.17 J/cm | 9.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 27.0 J | 19.9 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 29.0 J | 21.4 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 115 µm/m-°C @Temperature -40.0 - 40.0 °C |
63.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 115 µm/m-°C @Temperature -40.0 - 40.0 °C |
63.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 132 µm/m-°C @Temperature -40.0 - 40.0 °C |
73.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 133 µm/m-°C @Temperature -40.0 - 40.0 °C |
73.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.0 °C | 95.0 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 38.0 °C @Thickness 3.20 mm |
100 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ B65 G30 black IG Polyamide 6 (Nylon 6)
- Guarniflon SC 1100 Polytetrafluoroethylene Seal
- Lehmann & Voss LUVOCOM® 1105/CF/10/GR/10/TF/10-2 PEEK, with carbon fiber, PTFE, lubricant modified
- SolVin 271DF Polyvinyl Chloride General Purpose - Plasticized
- Shinil Chemical SHINFLAME PC/ABS Flame Retardant Polymer TV Housing
- A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene
- DSM Akulon® S223-G6 Nylon 66-30% Glass Reinforced (European and Asian Grade) (Cond)
- Arlon CP-499CA Bulk Compound
- Arlon 32300R062 0.062" (1.57 mm) Uncured Silicone Rubber on PET Carrier
Copyright © lookpolymers.com All Rights Reserved