SABIC Innovative Plastics LNP THERMOCOMP RF009S PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP RF009S PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* RF009S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Time 86400 sec
 0.0030 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 222 MPa
32200 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Tensile Modulus 16.56 GPa
2402 ksi
50 mm/min; ASTM D638
Flexural Strength 330 MPa
47900 psi
ASTM D790
Flexural Modulus 13.2 GPa
1910 ksi
ASTM D790
Izod Impact, Notched 1.54 J/cm
2.89 ft-lb/in
ASTM D256
Izod Impact, Unnotched 15.17 J/cm
28.42 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 252 °C

@Thickness 3.20 mm
 486 °F

@Thickness 0.126 in
 unannealed; ASTM D648