SABIC Innovative Plastics LNP THERMOCOMP RC008 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RC008 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RC008 is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 267 MPa | 38700 psi | ASTM D638 |
| 293 MPa | 42500 psi | ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| 1.9 % | 1.9 % | ASTM D638 | |
| Tensile Modulus | 29.5 GPa | 4280 ksi | 1 mm/min; ISO 527 |
| 30.7 GPa | 4450 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 439 MPa | 63700 psi | ASTM D790 |
| 457 MPa | 66300 psi | ISO 178 | |
| Flexural Modulus | 23.16 GPa | 3359 ksi | ASTM D790 |
| 28.4 GPa | 4120 ksi | ISO 178 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.1 J/cm | 20.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 74.0 kJ/m² | 35.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.30 | 0.30 | ASTM D3702 Modified |
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S75R Silicone Rubber
- Malvern Minerals Nylon with Novakup® L-337 Silane-Treated Quartz Filler
- Saint-Gobain Chemlam® SGC6-10 Copper Adhesive Tape
- Techmer ES HiFill® POM CO GF25 CC 25% Glass Filled
- Schott N-LAF7 Glass
- Teknor Apex Telcar® TL-87-L832A Thermoplastic Elastomer
- A. Schulman POLYBLAK™ 3225 Superior Black Color Concentrate, 50% Carbon Black Based In PP Homopolymer
- Chosun Refractories COD-2 Special brick
- CENTROPLAST CENTRODAL LF Polyoxymethylene conductive
- Polykemi AB POLYfill PPH BF405510 VT1 Polypropylene Homopolymer, Reinforced, Heat Resistant
Copyright © lookpolymers.com All Rights Reserved