SABIC Innovative Plastics LNP THERMOCOMP OF008E PPS - Linear (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP OF008E PPS - Linear (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* OF008E is a compound based on PPS - Linear resin containing Glass Fiber. Added features include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.012 cm/cm @Time 86400 sec |
0.0080 - 0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 177 MPa | 25700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.9 GPa | 1870 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 251 MPa | 36400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 12.3 GPa | 1780 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
12.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
27.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- RheTech Products HP522-00 15% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- Nabaltec APYMAG® 30S Magnesium Hydroxide
- Orion Engineered Carbons CORAX® N 683 ASTM Carbon Black
- Polykemi AB POLYabs F20 ABS
- LG Chemical XR401B ABS, High Flow, Heat Resistance
- LATI Laril 13 G/10-V1 PPOm, 10% Glass Fiber Reinforced, Flame Retardant
- Master Bond EP79FL Two Component Silver Nickel Conductive Epoxy Adhesive
- ExxonMobil Kutwell 82
- ArcelorMittal AS80 Aluminized steel
- Potters Industries A-Series A-170 Soda-Lime Silica Technical Quality Solid Glass Spheres
Copyright © lookpolymers.com All Rights Reserved