SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OF008A is a compound based on PPS - Branched resin containing Glass Fiber.This product is also known as Thermocomp* OF-1008.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| 178 MPa | 25800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 |
| 248 MPa | 36000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 13.4 GPa | 1940 ksi | 2 mm/min; ISO 178 |
| 14.26 GPa | 2068 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
14.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 272 °C | 522 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V70H Fluoroelastomer Compound
- PolyOne Geon™ HTX M6215 Polyvinyl Chloride Alloy (PVC Alloy)
- Less Common Metals Yttrium Vacuum Remelted Rare Earth Metal
- Kolon KOPA® KN333G15HI Multi Reinforced Nylon 66
- Techmer ES HiFill® PP 0475 Polypropylene
- Esstech X-947-7446 Trimethylolpropane Trimethacrylate, C18H26O6
- CLAL-MSX CUPROROR® TL4 Hard, Copper Alloy
- AK Steel 430 Ferritic Stainless steel
- Lushan PR-5 Maleic Anhydride Grafted Polypropylene
- PolyOne Synprene® RT-3620 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved