SABIC Innovative Plastics LNP THERMOCOMP OF008 PPS - Linear
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP OF008 PPS - Linear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* OF008 is a compound based on PPS - Linear resin containing 40% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| Tensile Modulus | 14.1 GPa | 2050 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 234 MPa | 33900 psi | ASTM D790 |
| Flexural Modulus | 14.22 GPa | 2062 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.50 | 0.50 | ASTM D3702 Modified |
| K (wear) Factor | 751 x 10-8 mm³/N-M | 373 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 264 °C @Thickness 3.20 mm |
507 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.450 mm |
V-0 @Thickness 0.0177 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- MV Labs RU470 {Ru(NH3)6}Cl2 Hexamineruthenium(II) chloride
- Nylene® 7250 C HS , 50% Glass Fiber/Ceramic Reinforced, Low Warp, High Stiffness Specialty Nylon
- Polyplastic Armlen® PP MF 25-3-901 Polypropylene, 20% Mineral Filled
- SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Europe-Africa-Middle East)
- Unitika elitel UE3300 Polyester, Flake
- 3M 7650-S-HSG Cold Shrink QT-III Silicone Rubber Skirted Termination Kits
- Akro-Plastic Akromid® T6 GF30 (3501) PPA Dry, 30% Glass Filled
- Ascend Performance Materials Vydyne® R543H Natural Nylon 66, 43% Glass Reinforced, DAM
- 3M Novec™ Contact Cleaner Plus
- Arlon 48571R006 0.0055" (0.140 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved