SABIC Innovative Plastics LNP THERMOCOMP MX06403 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MX06403 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MX06403 is a compound based on Polypropylene resin containing 20% Glass Fiber. Added features of this material include: Heat Stabilized, UV Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Time 86400 sec |
0.0050 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 66.0 MPa | 9570 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.93 J/cm | 5.49 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer (Asia Pacific)
- SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific)
- Shin-Etsu Silicones LIMSâ„¢ KE2090-70AB Elastomer
- Eagle Brass 706 Copper Nickel 10%, Spring
- Esstech X-733-0000 1,12 Dodecanediol Dimethacrylate, C20H34O4
- Abatron Metalfix-LH™ Aluminum-Filled, Structural Adhesive Putty; High Temperature Liquid
- Braskem EB 861/51 LDPE Blown Film Extrusion Polyethylene
- Bulk Molding Compounds BMC 5592 Arc, Track, and Weather Resistant Polyester
- Bhansali Engineering Abstron IM-17A(DLW) ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved