SABIC Innovative Plastics LNP THERMOCOMP ECF62 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ECF62 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* ECF62 is a compound based on Polyetherimide resin containing 30% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm @Time 86400 sec |
0.0030 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Tensile Modulus | 17.92 GPa | 2599 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 268 MPa | 38900 psi | ASTM D790 |
| Flexural Modulus | 15.85 GPa | 2299 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.85 J/cm | 9.09 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 23.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 - 1.00e+11 ohm-cm | 1.00e+10 - 1.00e+11 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3865A TPE, PP Overmold or Standalone use
- Nitriflex NP-1021 Powdered Nitrile
- Mar-Bal MB1000-25 Thermoset Polyester Composite Molding Compound
- Multibase Multibatch® ME 50009 Anti-blocking Masterbatch
- Sharadaa Ceramics REFCAST C SUPER High Alumina Castables
- Samsung Cheil Industries Starex® VE-0857 ABS, Unreinforced FR
- Plenco 1508 Polyester, Briquette, Transfer Molded
- A. Schulman PP 1632-01 Polypropylene Random Copolymer
- Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved