SABIC Innovative Plastics LNP THERMOCOMP EC006APQ PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EC006APQ PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp EC006APQ is a compound based on Polyetherimide containing 30% Carbon Fiber. Added features include: Electrically Conductive, High Flow.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00030 cm/cm @Time 86400 sec |
0.00030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 69 g/10 min @Load 6.70 kg, Temperature 380 °C |
69 g/10 min @Load 14.8 lb, Temperature 716 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 252 MPa | 36500 psi | 5 mm/min; ISO 527 |
| 281 MPa | 40800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.1 % | 1.1 % | 5 mm/min; ISO 527 |
| 1.1 - 1.3 % | 1.1 - 1.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 29.25 GPa | 4242 ksi | 1 mm/min; ISO 527 |
| 30.52 GPa | 4427 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 332 MPa | 48200 psi | ISO 178 |
| 350 MPa | 50800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 23.93 GPa | 3471 ksi | 2 mm/min; ISO 178 |
| 26.3 GPa | 3810 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Compressive Strength | 231 MPa | 33500 psi | SABIC Method |
| Poissons Ratio | 0.44 | 0.44 | ASTM E 132 |
| Shear Modulus | 4.726 GPa | 685.5 ksi | ASTM C273 |
| Shear Strength | 128 MPa | 18600 psi | ASTM C273 |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.13 J/cm | 13.4 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.00 µm/m-°C @Temperature -40.0 - 150 °C |
3.89 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 5.00 µm/m-°C @Temperature -40.0 - 150 °C |
2.78 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 ohm | 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- LyondellBasell Petrothene® LR734011 High Density Polyethylene (Sheet & Profile Extrusion)
- Gwent Electronic Materials C2090225D7 Silver/Silver Chloride Paste
- Taiwan Sheen Soon Sheenthane® AH-853 TPU for Hotmelt Adhesive
- Teknor Apex Monprene® MP-2815B Thermoplastic Elastomer
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 310ºF Cure Temperature
- Cossa Polimeri ESTAPROP 1006 V2 H Flame Retardant Polypropylene
- ExxonMobil Oppalyte™ 38ICE OPP Film
- Axiall 8910 Moldings & Extrusions Flexible PVC
- Beijing Chemical Industry KAIFA® 301-G20F PBT Resin
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber
Copyright © lookpolymers.com All Rights Reserved