- SABIC Innovative Plastics LNP THERMOCOMP EC005R PEI
SABIC Innovative Plastics LNP THERMOCOMP EC005R PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EC005R PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* EC005R is a compound based on Polyetherimide resin containing 25% Carbon Fiber. Added features include: Mold Release, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.180 % | 0.180 % | 23°C / 50% RH; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 179 MPa | 26000 psi | 5 mm/min; ISO 527 |
| 200 MPa | 29000 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | 5 mm/min; ISO 527 |
| 132 MPa | 19100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.70 % | 0.70 % | Type I, 5 mm/min; ASTM D638 |
| 1.0 % | 1.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 22.9 GPa | 3320 ksi | 1 mm/min; ISO 527 |
| 41.99 GPa | 6090 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 275 MPa | 39900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 18.56 GPa | 2692 ksi | 2 mm/min; ISO 178 |
| 19.08 GPa | 2767 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.19 J/cm | 9.72 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 24.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs NH200 NH4Br Ammonium bromide
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T700 Uni Tape Reinforced
- Plenco 304 Black Impact Grade Woodflour/Cellulose Filled Phenolic Molding Compound (discontinued **)
- Techmer ES Luriblend® PA6/6 CF30 TS15 BK 30% Carbon Filled
- Hexcel® HexPly® 954-3A Curing Cyanate Resin, M60J Fiber
- American Elements Barium Titanate nanoparticles
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 60A, Non-Black Peroxide Cure