SABIC Innovative Plastics LNP THERMOCOMP DF0049E PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF0049E PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF0049E is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0042 cm/cm @Time 86400 sec |
0.0042 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 101 MPa | 14600 psi | ASTM D638 |
| 102 MPa | 14800 psi | ISO 527 | |
| Tensile Strength, Yield | 102 MPa | 14800 psi | ASTM D638 |
| 102 MPa | 14800 psi | ISO 527 | |
| Elongation at Break | 3.1 % | 3.1 % | ISO 527 |
| 8.8 % | 8.8 % | ASTM D638 | |
| Elongation at Yield | 2.8 % | 2.8 % | ISO 527 |
| 2.9 % | 2.9 % | ASTM D638 | |
| Tensile Modulus | 7.38 GPa | 1070 ksi | 1 mm/min; ISO 527 |
| 7.58 GPa | 1100 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| 165 MPa | 23900 psi | ISO 178 | |
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
| 6.20 GPa | 899 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.33 J/cm | 15.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 56.0 kJ/m² | 26.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J | 13.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.20 µm/m-°C @Temperature -40.0 - 40.0 °C |
4.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 1.80 µm/m-°C @Temperature -40.0 - 40.0 °C |
1.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 25.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 146 °C @Thickness 3.20 mm |
295 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nitriflex SB-1013G Styrene Butadiene Copolymer
- PolyOne Edgetek® NY-20GF/10GB/000 Polyamide 6 (Nylon 6)
- Solvay Specialty Polymers KetaSpire® KT-820 GF13 Polyetheretherketone (PEEK) (Unverified Data**)
- Honeywell Capran® Emblem™ 1200 Bi-Axially Oriented Nylon Film
- Lehmann & Voss LUVOCOM® 80-7580 Polyacetal-copolymer, with aramid reinforcement and PTFE
- LG Chemical LUPOY SC1004L PC, High Impact
- Gromax BTE25-DN00N1 Nylon 6 (Dry)
- Styron DL 8806LA Carboxylated SB
- Zell-Metall Engineering Plastics Zellamid 250 GF 30 (PA6.6 + 30% glass fiber)
- A. Schulman POLYBLAK™ 4692 Premium Black Color Concentrate, 35% Carbon Black Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved