- Thermoset
- Polyester, TS
- Thermoset Polyester Glass SMC
- Premix Premi-Glas® 1201-15 Polyester SMC
Premix Premi-Glas® 1201-15 Polyester SMC
| Category | Polymer , Thermoset , Composite SMC , Polyester, TS , Thermoset Polyester Glass SMC |
| Manufacturer | Premix |
| Trade Name | Premi-Glas® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Premix Premi-Glas® 1201-15 Polyester SMC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Premi-Glas® 1201-15 is a 15% glass reinforced thermoset Sheet Molding Compound designed for sinks, shower stall bases and wall applications. Key features and benefits are:Supports ANSI 124.2 and CSA B45.5 requirements for flame, smoke and stain resistance. Available in glass contents ranging from 10% - 20%; standard product has 15% reinforcement. High gloss, non-rippling surface appearance on large flat surfaces and deep draw side walls. Excellent as-molded dimensional tolerances. Outstanding moldability and flow in compression process. Standard color is white.Passes ANSI 124.2/ CSA B,45.5 stain resistanceData provided by Premix.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 35.0 MPa | 5080 psi | ASTM D638 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 3.50 GPa | 508 ksi | Calculated |
| Izod Impact, Notched | 3.70 J/cm | 6.93 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.25 J/cm | 7.96 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | XY Direction |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 150 °C | 302 °F | Compression Molding |
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flame Resistance | pass at 3 mm | ANSI Z124.2 |
| Stain Resistance | pass | ANSI Z124.2 |
Users viewing this material also viewed the following:
- SABIC PP 513MN40 Polypropylene Impact Copolymer for Injection Molding
- Ineos H04G-00 Polypropylene Homopolymer
- Haynes 230® alloy, 30% cold reduction
- UBE 1022T Nylon 6 Monofilament (Drawing Ratio=5)
- A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene
- Unipetrol Winter Propane-Butane
- ExxonMobil Coolant/Antifreeze Mobil Heavy Duty 50/50 Prediluted
- Toyobo PELPRENE™ P95C Polyester TPE, High Flexibility, High Melting Point
- Eurotec® Tecomid® NA40 GR30 NL RT PA 6.6 30% glass fiber reinforced, very low friction and wear
- Eurotec® Tecomid® NA40 CR10 BK111 PA6.6, 10% carbon fiber reinforced, black
Copyright © lookpolymers.com All Rights Reserved