Category | Polymer , Thermoplastic , Polycarbonate (PC) |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | LNP THERMOCOMP |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DC004E PC (Europe-Africa-Middle East).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | on Tensile Bar; SABIC Method |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
Tensile Modulus | 12.2 GPa | 1770 ksi | 1 mm/min; ISO 527 |
Flexural Yield Strength | 227 MPa | 32900 psi | 2 mm/min; ISO 178 |
Flexural Modulus | 11.9 GPa | 1730 ksi | 2 mm/min; ISO 178 |
Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 9.00 µm/m-°C @Temperature 23.0 - 60.0 °C |
5.00 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |