SABIC Innovative Plastics LNP THERMOCOMP DC0049XF PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DC0049XF PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DC0049XF is a compound based on Polycarbonate resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.130 % | 0.130 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00030 - 0.00050 cm/cm @Time 86400 sec |
0.00030 - 0.00050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 132 MPa | 19100 psi | Type I, 5 mm/min; ASTM D638 |
| 133 MPa | 19300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 132 MPa | 19100 psi | Type I, 5 mm/min; ASTM D638 |
| 133 MPa | 19300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.64 GPa | 1833 ksi | 50 mm/min; ASTM D638 |
| 13.0 GPa | 1890 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 202 MPa | 29300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 202 MPa | 29300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.54 GPa | 1529 ksi | 2 mm/min; ISO 178 |
| 11.07 GPa | 1606 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.62 J/cm | 8.66 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 1.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
0.556 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 8.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
4.44 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CM200LN-02 Polypropylene Impact Copolymer
- Global PEI-110 Easy Flow, Polyetherimide
- Lucent Polymers PC/PBT-1550 Polycarbonate+PBT, Improved Impact Resistance, Injection Grade
- Stellarchem MP-8001 TPE Compound
- Zircar Ceramics ALBF Alumina Bulk Fiber
- Tra-Con Tra-Coat 15C UV Curable Coating Adhesive
- Polyplastics Duranex® 3300H Polybutylene Terephthalate (PBT), Standard, 30% GF filled
- ExxonMobil Oppera PR 100A (AM) Modifier
- Asahi Kasei Thermofil P-20TC-5100 20% Talc Filled, Heat Stabilized
- Abatron Ferrobond-P™ Steel-Filled, Structural Adhesive Putty; Paste
Copyright © lookpolymers.com All Rights Reserved