SABIC Innovative Plastics LNP STAT-LOY 63000CTU PC+POLYESTER (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY 63000CTU PC+POLYESTER (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A permanent antistatic PC-Alloy compound that features transparency, UV cut, and superior cleanliness for advanced semiconductor packaging applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 260 °C |
19 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Tensile Modulus | 1.16 GPa | 168 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 53.0 MPa | 7690 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.21 GPa | 175 ksi | ASTM D790 |
| Izod Impact, Notched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 6.90 J/cm² | 32.8 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C @Thickness 6.40 mm |
181 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C @Thickness 6.40 mm |
165 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 10 % @Thickness 2.54 mm |
10 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 35 % | 35 % | 3.0 mm; SABIC Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 - 5.00e+12 ohm-cm | 1.00e+11 - 5.00e+12 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+11 - 5.00e+12 ohm | 1.00e+11 - 5.00e+12 ohm | ASTM D257 |
| Static Decay | 2.0 sec | 2.0 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8960 (498A) (UF) Synthetic Oil
- SABIC Innovative Plastics Cycolac® MG38N ABS (Asia Pacific)
- 2074A Polyurethane-based Biomedical Elastomer
- MBA Polymers PP 2126 Post-consumer recycled general purpose polypropylene impact copolymer
- Momentive Performance Materials TSE 2297 Heat Cured Rubber - High Duro Translucent
- Styron Pulse® 930 ABS + Polycarbonate
- ConocoPhillips SynXPA® HC-450 H Lubricant HC-450
- Chengdu Polyster 8500 General Grade TPV
- Overview of materials for PC/ABS + Stainless Steel
- NOVA Chemicals Sclair® 11E1 Butene LLDPE Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved