SABIC Innovative Plastics LNP STAT-KON WE002 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON WE002 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* WE002 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0039 - 0.0056 cm/cm @Time 86400 sec |
0.0039 - 0.0056 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0091 - 0.0114 cm/cm @Time 86400 sec |
0.0091 - 0.0114 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| 133 MPa | 19300 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.5 % | 2.5 % | ASTM D638 | |
| Tensile Modulus | 10.14 GPa | 1471 ksi | 50 mm/min; ASTM D638 |
| 10.46 GPa | 1517 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 181 MPa | 26300 psi | ASTM D790 |
| 184 MPa | 26700 psi | ISO 178 | |
| Flexural Modulus | 7.39 GPa | 1070 ksi | ASTM D790 |
| 7.76 GPa | 1130 ksi | ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.37 J/cm | 8.19 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 41.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 79.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Geon™ HTX Ultra LA425 Polyvinyl Chloride Alloy (PVC Alloy)
- Overview of materials for Polycarbonate/ABS Alloy, Glass Fiber Filled
- Dow Corning SILASTIC® LS 5-8725 FLUOROSILICONE RUBBER
- ChevronTexaco Geotex® LA SAE 30
- Clariant 6618G15 HSL UV Black Nylon 66, 15% Glass Fiber, Impact Modified, UV and Heat Stabilized, Lubricated
- ATI Wah Chang 425™ Titanium Alloy, Solution Treated Annealed Bar 0.5 - 1.23 in. dia
- Axiall 15642 Wire & Cable Flexible PVC
- 3M 1182 EMI Shielding Tape
Copyright © lookpolymers.com All Rights Reserved