SABIC Innovative Plastics LNP Lubricomp UX06442 PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp UX06442 PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* UX06442 is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.40 % @Time 86400 sec |
0.40 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.014 cm/cm @Time 86400 sec |
0.012 - 0.014 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.015 - 0.017 cm/cm @Time 86400 sec |
0.015 - 0.017 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527 |
| 81.0 MPa | 11700 psi | ASTM D 638 | |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 |
| 3.5 % | 3.5 % | ASTM D 638 | |
| Tensile Modulus | 2.677 GPa | 388.3 ksi | 1 mm/min; ISO 527 |
| 3.95 GPa | 573 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 129 MPa | 18700 psi | ASTM D 790 |
| Flexural Modulus | 3.41 GPa | 495 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.260 J/cm @Temperature 23.0 °C |
0.487 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.23 J/cm @Temperature 23.0 °C |
9.80 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Coefficient of Friction, Dynamic | 0.23 | 0.23 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.21 | 0.21 | ASTM D 3702 Modified |
| K (wear) Factor | 14.1 x 10-8 mm³/N-M | 7.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 62.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 0.46 MPa (66 psi) | 234 °C @Thickness 3.20 mm |
453 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Old Hickory FC-120 Tennessee Ball Clay
- MMCC Al/Al2O3 Continuous Fiber Aluminum Matrix Composite
- SABIC Innovative Plastics LNP LUBRICOMP UX06427 PPA
- Total Lumicene® mPE M5220 Metallocene High Density Polyethylene
- Wolf Kunststoff ZEDEX® ZX-530CD3 031 Polymer Alloy, Fiber Reinforced and PTFE Modified
- Tra-Con Tra-Bond Ablebond 744-2NTN1 Electrically Insulating Polyimide Adhesive
- Axiall 19732 Wire & Cable Flexible PVC
- Dow Corning 2-9034 EMULSION
- Loctite® 572 Low Strength Thread Sealant
- BP Amoco Acctuf® 3240 Impact Copolymer Polypropylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved