SABIC Innovative Plastics LNP Lubricomp UCL36AS PPA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp UCL36AS PPA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* UCL36AS is a compound based on Polyphthalamide resin containing Carbon Fiber, PTFE. Added features include; Internally Lubricated, Electrically Conductive, Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % @Temperature 23.0 °C, Time 86400 sec |
0.40 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0015 cm/cm | 0.00050 - 0.0015 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 256 MPa | 37100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.3 % | 1.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 25.1 GPa | 3640 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 340 MPa | 49300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 19.9 GPa | 2890 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C @Temperature 23.0 - 60.0 °C |
4.44 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
28.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9960C TPE, ABS/PC Overmold
- Palm Labs Adhesives Turbo Fuse Series 140 (200 Viscosity) Rapid Bonding Adhesive
- SABIC Innovative Plastics Lexan® 203R PC (Europe-Africa-Middle East)
- LATI Latamid 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized
- SYNTHOS Kralex® 1501 Styrene Butadiene Rubber
- Solvay Specialty Polymers Solvera® PT 5071 PFPE Surface Treatment
- Styrolution Novodur® E401 ABS
- A. Schulman PP 3471-01 Polypropylene High Flow Homopolymer Polypropylene
- DuPont Performance Polymers Zytel® 70G13HS1L BK031 Nylon 66 (Unverified Data**)
- Fainplast Compounds GS 55/KSN Flexible PVC, Injection Molding for Transparent Technical Items
Copyright © lookpolymers.com All Rights Reserved